Effect of hyperbaric oxygen profiles on the bond strength of repaired composite resin


1 Department of Restorative Dental Sciences, Alfarabi Colleges, Riyadh, Saudi Arabia
2 Department of Preventive Dental Sciences, Alfarabi Colleges, Riyadh, Saudi Arabia

Correspondence Address:
Hossam Mossa
Department of Restorative Dental Science, Alfarabi Colleges, Riyadh - 11691
Saudi Arabia
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/2231-0762.181189

Rights and Permissions

Objective: This study was performed to evaluate the bond strength of repaired three types of composite resins under various hyperbaric oxygen (HBO) profiles with various session numbers. Materials and Methods: Sixty specimens of three types of composite resin (nanofilled composite, nanohybrid composite and microfilled composite) each type of composite was divided into four group according to various profiles of HBO treatment (control, 2bar, 3 bar and 5 bar). Then, the specimens were repaired; thermocycled, the tensile bond strength were measured. Then the data were analyzed by One-way ANOVA followed by Tukey's post hoc test (α = 0.05). Results: The highest bond strength was obtained for the repaired nanofilled composite resin specimens while; the lowest bond strength was obtained for the repaired microfilled composite resin specimens. The highest tensile bond strength was recorded for the specimens who treated with the highest pressure of HBO. Conclusion: The bond strength of repaired nanofilled composite resins is better than the other types of composite resin. The highest pressure of HBO, the highest bond strength of repaired composite resins.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed801    
    Printed4    
    Emailed0    
    PDF Downloaded63    
    Comments [Add]    

Recommend this journal