ORIGINAL ARTICLE
Year : 2017  |  Volume : 7  |  Issue : 1  |  Page : 34-40

Analysis of the mechanical behavior and surface rugosity of different dental die materials


Department of Restorative Dentistry, São Leopoldo Mandic Dental School, Campinas-São Paulo, Brazil

Correspondence Address:
Simone Kreve
Department of Restorative Dentistry, São Leopoldo Mandic Dental School, Campinas-São Paulo
Brazil
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/2231-0762.200706

Rights and Permissions

Aim: This work evaluated the mechanical and surface behavior of different die materials. The studied materials are polyurethane resin Exakto-Form (Bredent), Gypsum type IV, Fuji Rock EP (Gc), and Durone (Dentsply). Materials and Methods: Two metallic matrices molded in polyvinyl siloxane provided 30 cylindrical test specimens for the diametral compression test and 30 hemispherical test specimens for the surface rugosity test. The cylindrical test specimens were submitted to tests of diametral compression strength using a DL2000 universal assay machine, with a load cell of 2000 Kgf and constant speed of 1 mm/min connected to the software. Kruskal–Wallis and Dunn's nonparametric tests were used to analyze the results. The hemispheres were submitted to the surface rugosity assay using a SJ201-P rugosimeter with a sensitivity of 300 μm, speed of 0.5 mm/s, and cut-off of 0.8 mm, and the readings were taken on the convex surface of the test specimens and metallic matrix. Results were analyzed using with Fisher's least significant differences test (LSD) and Dunnett's test. Results: Kruskal–Wallis test showed significant difference between die materials for diametral compression strength (P = 0.002). Dunn's test showed significantly higher values for modified polyurethane resin (Exakto-Form). The gypsum type IV, which did not significantly differ regarding diametral compression strength, showed 34.0% (Durone) and 42.7% (Fuji Rock) lower values in comparison to Exakto-Form. Conclusion: Within the parameters adopted in this study, it is possible to conclude that Exakto-Form polyurethane resin showed higher resistance to compression and was closer to the metallic matrix rugosity, and, along with the gypsum type IV Durone, showed better reproducibility of details relative to the Fuji Rock.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed249    
    Printed9    
    Emailed0    
    PDF Downloaded11    
    Comments [Add]    

Recommend this journal