| Abstract|| |
Background and Aims: This study aimed to investigate the remineralization potential of two concentrations of theobromine (100mg/L and 200 mmg/L) with fluoridated dentifrice, NovaMin, and nanohydroxyapatite using DIAGNOdent, scanning electron microscopy (SEM), and energy dispersive X-ray (EDX) analysis. Materials and Methods: Two sections were taken from 50 teeth each. Artificial carious lesions were induced using demineralizing solution. Evaluation using DIAGNOdent, SEM, and EDX analysis for elemental evaluation of Ca/P ratio and fluoride ion was carried out. Teeth sections were then randomly assigned to five different groups: (1) fluoridated dentifrice (ColgateTM, Colgate –Palmolive, India), Novamine- Shy NMTM, Group pharamaceuticals, India), 3. Nano-hydroxyapatite- Remin ProTM, Voco, Germany) 4. 100mg and 5. 200mg of Theobromine toothpaste (Theodent classicTM, Rennou, UK-853069003006). Remineralization was carried out for 14 days with two applications per day. Samples were reanalyzed using DIAGNOdent, SEM, and EDX. Results: A Tukey post-hoc test revealed statistically significant difference between NovaMin and all the other toothpastes (P < 0.001) for DIAGNOdent readings. On performing SEM-EDX analysis, it was seen that all agents had remineralization potential; however, no significant difference was found. Conclusion: Theobromine can be used as an effective novel remineralizing agent alternative to the already-available agents.
Keywords: Nanohydroxyapatite, NovaMin, remineralization, theobromine
|How to cite this URL:|
Taneja V, Nekkanti S, Gupta K, Hassija J. Remineralization potential of theobromine on artificial carious lesions. J Int Soc Prevent Communit Dent [Epub ahead of print] [cited 2019 Nov 20]. Available from: http://www.jispcd.org/preprintarticle.asp?id=270229
| Introduction|| |
Regardless of the age, gender, and ethnicity, dental caries is a complex disease affecting a majority population of the world. Dental caries is a continuous process, which starts from the first atomic level of demineralization, progresses to initial white spot, and often can cause dentinal involvement eventually leading to cavitation. The dynamic balance between demineralization and remineralization, as determined by pathological factors and protective factors, determines the end result. As the disease of dental caries is reversible so if diagnosed early enough, various antibacterial and chemical methods can be used to facilitate remineralization and reduce demineralization.
Remineralization may be as simple as the immediate repair of recently acid damaged enamel and occur on need basis with no clinical evidence of a lesion. Conversely, the repair process may require prolonged mineral deposition in order to reverse a clinically detectable white-spot lesion (WSL). It is important to realize that remineralization is an ongoing process in the oral cavity. The fate of the lesion, whether it will progress to cavitate or remineralize, depends on biological factors in the plaque and saliva, composition of enamel, oral hygiene, dietary habits, and exposure to preventive agents.
Calcium, phosphate, and fluoride can act together and reverse demineralization, by depositing a new layer on the crystal remnants. The new mineral surface is more acid resistant as compared with the original carbonated hydroxyapatite mineral. The demineralization–remineralization cycle occurs numerous times daily, leading either to cavitation or to repair and reversal. The mainstay in caries prevention and remineralization is frequent exposure to low levels of fluoride. Thus, many novel remineralizing agents are being introduced for the well-being of the society.
Few novel remineralizing agents are nanohydroxyapatite, NovaMin, and theobromine, which help in remineralization by various mechanisms.
Nanohydroxyapatite (n-HAp) is considered one of the most biocompatible and bioactive materials, and has gained wide acceptance in dentistry in recent years. Hydroxyapatite acts as a calcium–phosphate reservoir, which helps to maintain a state of supersaturation with respect to enamel minerals and hence reduces enamel demineralization and enhances remineralization.
NovaMin is a bioactive glass that acts as a biomimetic mineralizer matching the body’s own mineralizing traits while also affecting cell signals in a way that benefits the restoration of tissue structure and function.
According to Arman Sadeghpour from Tulane University, New Orleans, LA, one of the alkaloids found in chocolate (240mg/cup) and cocoa (1.89%), theobromine, can be used to prevent demineralization of enamel. Theobromine (3,7 dimethylxanthine) is a chemical compound of the alkaloid group in the form of white crystalline powder and only differs from the caffeine molecule by one methyl group (1, 3, 7 dimethylxanthine). It decreases caries or promotes remineralization by enhancing crystallinity. It is a nontoxic, natural, and an effective remineralizing agent. As theobromine causes calcium and phosphate from saliva to combine into a crystal unit four times larger than hydroxyapatite, growth of new enamel is stimulated. Another theory states that adding theobromine to apatite material can increase the size of crystallite size. Theobromine had shown increased hardness of enamel after its application followed by experimental demineralization of enamel.,,
As there is a limited literature available on remineralization potential of theobromine, this study was designed to determine its efficacy in remineralizing the artificially created incipient enamel lesions. The aim of this study was to investigate the remineralization potential of two concentrations of theobromine (100mg/L and 200 mmg/L) with fluoridated dentifrice, NovaMin, and n-HAp using DIAGNOdent, scanning electron microscopy (SEM), and energy dispersive X-ray (EDX) analysis.
Theobromine may have a similar remineralizing effect as that of fluoridated dentrifrice and other remineralizing agents used in this study.
| Materials and Methods|| |
Type Of Study
This is an in vitro experimental study. Sample size was estimated using the power calculation α = 0.05 and β = 0.20 with 80% being the power of the study, based on previous findings reported by Hegde and Moany:
A sample size of 50 was deemed essential. A total of 200 primary molars indicated for extraction were obtained from patients aged 3–14 years who reported to the Department of Pedodontics and Preventive Dentistry, Manipal College of Dental Sciences (MCODS), Manipal, Karnataka, India. Owing to the difficulty in obtaining intact teeth, teeth with at least two surfaces intact were selected, 50 such teeth were selected, and these were then divided randomly into five groups: Group 1: flouride; Group 2: NovaMin; Group 3: n-HAp; Group 4: theobromine 100mg/mL; and Group 5: theobromine 200mg/mL. Samples were cleaned off any debris. With the help of micromotor hand piece and diamond disk, the samples were sectioned and roots were separated. Crowns were sectioned into two parts and were grouped as demineralized or remineralized sample. Two halves of same tooth were used for both deminearlization and remineraization. Total duration of the study was two months.
Induction Of Artificial Carious Lesions
All the samples were immersed in 12-mL demineralizing solution for 72h. The composition of demineralizing solution used is as follows: 2.2-mM CaCl2, 2.2-mM NaH2PO4, 0.05-M lactic acid, and 0.2-ppm fluoride. The pH was adjusted to 3 with 50% NaOH. One sample was immersed in each bottle and then stored for 72h at 37°C.
DIAGNOdent recordings were taken at this stage as per the manufacturer’s instructions [Table 1].
Further for a better surface morphology analysis, all the samples were gold sputtered. For surface morphology evaluation, samples were subjected to SEM analysis. Following this, for elemental analysis for calcium, phosphate, and fluoride, EDX analysis was carried out (SEM-EDX, ZEISS EVO MA18, Oxford EDS, and X-act) at 15kV and ×500, ×1000, ×1500, ×2000, and ×2500 magnification [Figure 1].
|Figure 1: SEM images after demineralization and remineralization in all the groups|
Click here to view
Application Of Test Agents
Test agents, Group I (fluoride dentrifrice: ColgateTM, Colgate-Palmolive, Mumbai, India), Group II (Novamine: SHY-NMTM, Group Pharmaceuticals, Bangalore, India), and Group III (n-HAp: Remin ProTM, Voco, Cuxhaven, Germany), were used in paste form. Groups IV and V were prepared by dissolving 100 and 200mg of theobromine toothpaste (Theodent ClassicTM, Rennou, London, UK) measured in 1L of artificial saliva. Respective test agents were applied on the samples at 24-h interval for 14 days. A cotton tip applicator was used to apply the respective agents on the samples according to manufacturer’s instructions. Samples were washed and stored in deionized water itself. Deionized water was changed every 24h.
After 14 days of remineralization regime, the surface was assessed using DIAGNOdent (KaVo DIAGNOdent 2095, Kaltenbach & Voigt GmbH & Co. KG, Germany) to record the values. The samples were also assessed using SEM-EDX (ZEISS EVO MA18, Oxford EDS, X-act) to study the change in surface characteristics and estimate the mineral content of calcium, phosphate, and fluoride [Figure 1] and [Figure 2].
|Figure 2: SEM images after demineralization and remineralization in all the groups|
Click here to view
| Statistical Analysis|| |
Data were entered in a dataspread sheet using the Statistical Package for the Social Sciences software version 18.0 (SPSS, Chicago, IL). Statistical analysis for DIAGNOdent readings was performed using post-hoc Tukey’s honestly significant difference and one-way analysis of variance (ANOVA). A value of P < 0.001 was considered statistically significant. Elemental analysis was carried out using Kruskal–Wallis ANOVA and Wilcoxon signed rank test. A value of P < 0.05 was considered statistically significant.
| Results|| |
DIAGNOdent readings were seen to increase following induction of WSLs and reduced following remineralization. The mean percentage difference between DIAGNOdent readings for Groups I, II, III, IV, and V increased to 60.74 ±10.94, 31.99 ± 10.05, 65.48 ± 11.66, 66.27 ± 10.00, and 62.97 ± 9.41 [Table 2].
|Table 2: Mean percentage difference in DIAGNOdent readings post-demineralization and post-remineralization in various groups|
Click here to view
A Tukey post-hoc test revealed that the mean percentage change was statistically significant between Novamine and all the other toothpastes (P < 0.001) with 95% confidence interval, but there was no statistically significant difference in mean percentage change between n-HAp, theobromine (100mg/mL), fluoride, and theobromine (200mg/mL), indicating that n-HAp, theobromine (100mg/mL), fluoride, and theobromine (200mg/mL) were broadly similar in terms of effectiveness [Table 3]. [Figure 1] shows the SEM analysis.
|Table 3: Intergroup comparison of DIAGNOdent readings post-demineralization and post-remineralization in various groups|
Click here to view
After 72h of demineralization, SEM images were taken. There was a loss of surface integrity in all the study groups. Enamel showed irregular surface like a honeycomb pattern. Porous defects could be seen, thus proving loss of aprismatic enamel and presence of destructed enamel rods.
After a 14-day remineralization regimen, samples were again subjected to SEM examination. The porous defects were all filled; thus, the surface integrity was reestablished. However, no distinct difference could be seen among the various groups, with regard to the surface coatings that filled the porosities.
Energy Dispersive X-Ray Analysis
EDX analysis was used to determine calcium, phosphorous, and fluoride contents in weight percent (wt%) of demineralized and remineralized enamel in all samples of each experimental group. The calcium and phosphorus content was then converted into Ca/P ratios for each group from the obtained data [Table 4] and [Table 5].
|Table 4: Intergroup comparison of mean percentage difference of Ca/P ratio post-demineralization and post-remineralization|
Click here to view
|Table 5: Intragroup comparison of mean percentage difference of Ca/P ratio post-demineralization and post-remineralization|
Click here to view
Using the same EDX analysis increase in fluoride ion concentration following remineralization was calculated [Table 6]. Comparing the mean concentration difference of fluoride ion between various groups was carried out using Kruskal–Wallis ANOVA test. No statistically significant difference was seen for mean concentration difference of fluoride ion for all groups with P-value 0.75 with 95% confidence interval. Mean percentage difference of Ca/P ratio between demineralization and remineralization of each group using Wilcoxon signed rank test. Statistically significant increase was seen for Group 1 between demineralization and remineralization.
|Table 6: Intragroup comparison of mean percentage difference of fluoride ion concentration post-demineralization and post-remineralization|
Click here to view
| Discussion|| |
Enamel remineralization has been studied for about 100 years, and it has been suggested that “the noninvasive” treatment of early caries lesions by remineralization has the potential to be the major advance in the clinical management of the disease. WSLs represent the first clinical observation of demineralization in enamel and their early diagnosis has been reported in the literature. DIAGNOdent is one of the recent noninvasive methods to detect early WSLs. However, in vitro and in vivo studies conducted to evaluate the efficacy of this laser device have given substantially varying results.,, For this study, probe B of DIAGNOdent was used. Prior to every measurement session, the instrument was calibrated against its own ceramic standards as recommended by manufacturer. The tip was moved over the entire tooth surface to collect the fluorescence from all directions and the maximum value was taken.
DIAGNOdent examination was carried out at room temperature 22°C which was according to a study by Shi et al., In accordance with a study by Pinelli et al., samples were dried for 10s before the examination. Following remineralization values decreased which was similar to results by Leila where values decreased for both n-HAp and fluoride but no significant difference was seen between two. Shi et al. have also showed similar results. No studies till date have evaluated the remineralization potential of NovaMin and theobromine with DIAGNOdent. According to this study, the values decreased for both the groups following remineralization. However, a significant difference was seen between NovaMin and other groups viz. fluoride, n-HAp, and both the concentrations of theobromine. No significant difference was found while comparing the other groups.
Various demineralizing agents have been used till date, in this study, demineralization was carried out as described by Lata et al. The specimens were kept in the demineralization solution (CaCl2, NaH2PO4, lactic acid, and fluoride) for 72h at 37°C creating a subsurface demineralization of approximately 150 µm width with an intact surface simulating an early enamel lesion. In this study, fluoride, NovaMin, and n-HAp were used in commercially available paste form. This was carried out in view of replication of patient convenience in using the tooth creams like a toothpaste with toothbrushes. Theobromine was used in two concentrations, 100mg/mL and 200mg/mL, which were prepared by mixing requisite amount of Theodent toothpaste (Theodent ClassicTM) in artificial saliva. The agents were applied with cotton tip applicator for 2min twice daily at 12-h interval. Samples were immersed in deionized water after each treatment till the next cycle of agent application. Samples were analyzed using SEM as it is one of the most sensitive, time-tested techniques to assess the demineralization and remineralization of the carious lesions in vitro as reported in earlier studies., Samples were dried and gold sputtered. To avoid the loss of samples, samples were sectioned into two halves and were examined at different magnifications. At ×1000 magnification, numerous depressions in a honeycomb pattern were revealed, which corresponded to the observations made by previous study. With the observation of SEM images, it could be said that DIAGNOdent also has similar credibility. Post-remineralization, all the samples showed reestablishment of surface integrity with increase in crystal size and occlusion of porous defects. However, there were minor differences among all the groups which could be because of their different mechanisms of remineralization. The SEM findings were in accordance with previous studies.,,
Similar to a study by Huang et al., the porous defects formed on demineralization were filled on remineralization using NaF and n-HAp. Although Swaroop et al. reported that n-HAP gave significantly better results, this can be attributed to preparation of fresh slurry in their study as compared with use of commercial toothpastes in this study. Similarly, Amechi  on evaluating SEM images post-remineralization claimed that crystal size increased post-remineralization on using theobromine as a remineralizing agent, thus giving the enamel surface a more uniform appearance. Although in a study by Kargul et al. on comparing the surface topography of enamel following application of 200mg/L of theobromine and 100mg/L of theobromine, 200mg/L was found to have better results; in our study, no such difference could be seen. This could be attributed to 5-min application in that study as compared with 2-min application in our study. Mony et al. on interpreting SEM images of samples remineralized with NovaMin and fluoride concluded that following remineralization, NovaMin gave smoother and uniform enamel, whereas formation of Fluoroapatite following fluoride application resulted in irregular enamel where defects were not uniformly covered. There is a lack of remineralization studies assessing the fluoride gain by EDX analysis. In this study, increase in the fluoride content post-remineralization was seen in all the groups; however, there was a statistically significant increase in fluoride content post-remineralization for Group I and statistically nonsignificant increase was seen for Groups II, III, IV, and V with P-values 0.20, 0.28, 0.33, and 0.28, respectively. A significant difference was seen in the fluoride content between Group I and other groups. In this study, all the groups showed a significant increase in the Ca/P ratio following remineralization; however, no statistically significant difference was seen between the groups. This is in agreement with previous studies that showed the capability of the chosen test agents to induce remineralization of early enamel lesions. The results were in accordance with Mohanty et al. where remineralization potential of NovaMin to a control was analyzed. The samples were analyzed at 0 days, 48h, and 10 days. A significant increase for Ca/P ratio was seen on EDX evaluation for NovaMin. Contrary to the results of this study, Swaroop in their study concluded that on performing the elemental analysis a significant increase was seen for n-HAp as compared with sodium fluoride. This could be attributed to the use of freshly prepared slurry of the agents as compared with the commercial toothpaste used in this study. A elemental analysis comparison carried out for theobromine and fluoride showed an increase in the Ca/P ratio without any significant difference, which was similar to result shown by Amechi in an in vitro experimental study conducted by Irawan et al. Suryana et al. and Sulistianingsih et al. revealed that there was an increase in enamel microhardness of enamel after application of theobromine gel. These findings are in consistent with our results where we found a significant increase in Ca/P ratio post application. Nakamoto et al. stated that theobromine-containing toothpastes can be used as an effective alternative to fluoride-containing dentifrices.
A limitation of this study is the lack of SEM-EDX analysis for the baseline samples and small sample size owing to the cost constraint. SEM-EDX at baseline could have facilitated a better comparison of the ability of the test agents to induce remineralization and their potential to bring the mineral content closer to baseline levels. In this study, superiority of one agent could not be established. Further in vivo studies with large sample size are recommended for evaluation of remineralization potential of Theobromine.
| Conclusion|| |
The following conclusions can be drawn based on this study:
- All test agents showed remineralization potential.
- No significant difference was seen between the remineralization potential of the test agents.
- Theobromine can be used as an effective alternative to the already-available remineralizing agents.
Data Availability Statement
Data will be available on request from corresponding author (Nekkanti Sridhar, firstname.lastname@example.org).
Financial Support And Sponsorship
This study was partially supported by Indian Council of Medical Research, Government of India, New Delhi [grant number 3/2/NOV.2014/PG-THESIS-HRD(23)].
Conflicts of interest
There are no conflicts of interest.
| References|| |
Hicks J, Frankiln GG, Catherine F. Biological factors in dental caries enamel structure and the caries process in the dynamic process of demineralization and remineralization (Part 1). J Clin Pediatr Dent 2005;28:119-24.
Roveri N, Battistella E, Foltran I, Foresti E, Iafisco M, Lelli M, et al
. Synthetic biomimetic carbonate-hydroxyapatite nanocrystals for enamel remineralization. Adv Mater Res 2008;47:821-4.
Reynolds EC. Calcium phosphate-based remineralization systems: Scientific evidence? Aust Dent J 2008;53:268-73.
Amechi BT. Remineralization of artificial enamel lesions by theobromine. Caries Res 2013;47:399-405.
Amaechi BT, Mathews SM, Mensinkai PK. Effect of theobromine-containing toothpaste on dentin tubule occlusion in situ
. Clin Oral Investig 2015;19:109-16.
NakamotoT. Theobromine increases crystal size; 2012. Available from: http://iadr.confex.com/iadr/2002SanDiego/techprogram/abstract_12740.htm. [Last accessed on 2012 Aug 15].
Irawan MI, Noerdin A, Eriwati YK. The effect of time in the exposure of theobromine gel to enamel and surface hardness after demineralisation with 1% citric acid. Int J Phys 2017;884:12005.
Duraisamy Y, Chaly PE, Priyadarshini VI, Mohammed J. Evaluation of remineralising potential of theobromine on human enamel surfaces: An in vitro
study. Int J Sci Res 2018;6:128-32.
Suryana M, Irawan B, Soufyan A. The effects of toot pasts containing theobromine and hydroxyapatite on enamel micro hardness after immersion in carbonated drink. Int J Phys 2018;1073:32010.
Hegde MN, Moany A. Remineralization of enamel subsurface lesions with casein phosphopeptide-amorphous calcium phosphate: A quantitative energy dispersive X-ray analysis using scanning electron microscopy: An in vitro
study. J Conserv Dent 2012;15:61-7.
] [Full text]
Lata S, Varghese NO, Varughese JM. Remineralization potential of fluoride and amorphous calcium phosphate-casein phospho peptide on enamel lesions: An in vitro
comparative evaluation. J Conserv Dent 2010;13:42-6.
] [Full text]
Daculsi G, Kerebel B, Kerebel LM. Mechanisms of acid dissolution of biological and synthetic apatite crystals at the lattice pattern level. Caries Res 1979;13:277-89.
Goel A, Chawla HS, Gauba K, Goyal A. Comparison of validity of DIAGNOdent with conventional methods for detection of occlusal caries in primary molars using the histological gold standard: An in vivo
study. J Indian Soc Pedod Prev Dent 2009;27:227-34.
] [Full text]
Reynolds EC. Calcium phosphate-based remineralization systems: Scientific evidence? Aust Dent J 2008;53:268-73.
Sridhar N, Tandon S, Rao N. A comparative evaluation of DIAGNOdent with visual and radiography for detection of occlusal caries: An in vitro
study. Indian J Dent Res 2009;20:326-31.
] [Full text]
Shi XQ, Welander U, Angmar-Månsson B. Occlusal caries detection with KaVo DIAGNOdent and radiography: An in vitro
comparison. Caries Res 2000;34:151-8.
Pinelli C, de Castro MLL, Serra MC. Effect of drying on the reproducibility of DIAGNOdent to detect caries-like lesions. Braz Dent J 2010;21:405-10.
Leila P. Effect of different topical agents on remineralization of early enamel lesion: An in vitro
study. J Dent Sch 2015;33:269-76.
Shi XQ, Tranaeus S, Angmar-Månsson B. Comparison of QLF and DIAGNOdent for quantification of smooth surface caries. Caries Res 2001;35:21-6.
Yamaguchi K, Miyazaki M, Takamizawa T, Inage H, Moore BK. Effect of CPP-ACP paste on mechanical properties of bovine enamel as determined by an ultrasonic device. J Dent 2006;34:230-6.
Kargul B, Özcan M, Peker S, Nakamoto T, Simmons WB, Falster AU. Evaluation of human enamel surfaces treated with theobromine: A pilot study. Oral Health Prev Dent 2012;10:275-82.
Huang SB, Gao SS, Yu HY. Effect of nano-hydroxyapatite concentration on remineralization of initial enamel lesion in vitro
. Biomed Mater 2009;4:202-8.
Saranya M. Comparative evaluation of the remineralizing efficacy of calcium sodium phosphosilicate agent and fluoride based on quantitative and qualitative analysis. J Indian Soc Pedod Prev Dent 2015;33:291-5.
Swaroop JS. Enamel surface remineralization: Using synthetic nanohydroxyapatite. Contemp Clin Dent 2002;3:433-6.
Pritam M. An in vitro
evaluation of remineralization potential of Novamin® on artificial enamel sub-surface lesions around orthodontic brackets using energy dispersive X-ray analysis (EDX). J Clin Diagn Res 2014;8:88-91.
Sulistianingsih S, Irmaleny I, Opik TH. The remineralisation potential of cocoa bean extract (theobroma cacao) to increase the enamel micro hardness. Padjadjaran J Dent 2017;29:107-12.
Nakamoto T, Falster AV, Simmons Jr WB. Theobromine: A safe and effective alternative for fluoride in dentifrices. J Caffeine Res 2016;6:1-9.
[Figure 1], [Figure 2]
[Table 1], [Table 2], [Table 3], [Table 4], [Table 5], [Table 6]