The effect of plasma surface treatment on the bioactivity of titanium implant materials (in vitro)


Ramy A Abdelrahim1, Nadia A Badr2, Kusai Baroudi3 
1 Department of Dental Biomaterials, School of Dentistry, Al-Azhar University, Cairo, Egypt; Department of Restorative Dental Sciences, Alfarabi Colleges, Riyadh, Saudi Arabia
2 Department of Dental Biomaterials, Cairo University, Cairo, Egypt
3 Department of Dental Sciences, Alfarabi Colleges, Riyadh, Saudi Arabia

Correspondence Address:
Kusai Baroudi
Department of Preventive Dental Sciences, Alfarabi Colleges, PO Box 85184, Riyadh - 11691
Saudi Arabia

Background: The surface of an implantable biomaterial plays a very important role in determining the biocompatibility, osteoinduction, and osteointegration of implants because it is in intimate contact with the host bone and soft tissues. Objective: This study was aimed to assess the effect of plasma surface treatment on the bioactivity of titanium alloy (Ti—6Al—4V). Materials and Methods: Fifteen titanium alloy samples were used in this study. The samples were divided into three groups (with five samples in each group). Five samples were kept untreated and served as control (group A). Another five plasma samples were sprayed for nitrogen ion implantation on their surfaces (group B) and the last five samples were pre-etched with acid before plasma treatment (group C). All the investigated samples were immersed for 7 days in Hank's balanced salt solution (HBSS) which was used as a simulating body fluid (SBF) at pH 7.4 and 37°C. HBSS was renewed every 3 days. The different surfaces were characterized by X-ray diffraction (XRD), Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM), Energy-dispersive X-ray spectroscopy (EDXA), and Fourier Transformation Infrared Spectroscopy (FTIR). Results: Nitriding of Ti-alloy samples via plasma nitrogen ion implantation increased the bioactivity of titanium. Moreover, the surface topography affected the chemical structure of the formed apatite. Increasing the surface roughness enhanced the bioactivity of the implant material. Conclusions: Nitridation can be exploited as an effective way to promote the formation of bone-like material on the implant surface.


How to cite this article:
Abdelrahim RA, Badr NA, Baroudi K. The effect of plasma surface treatment on the bioactivity of titanium implant materials (in vitro).J Int Soc Prevent Communit Dent 2016;6:15-21


How to cite this URL:
Abdelrahim RA, Badr NA, Baroudi K. The effect of plasma surface treatment on the bioactivity of titanium implant materials (in vitro). J Int Soc Prevent Communit Dent [serial online] 2016 [cited 2021 Jan 17 ];6:15-21
Available from: https://www.jispcd.org/article.asp?issn=2231-0762;year=2016;volume=6;issue=1;spage=15;epage=21;aulast=Abdelrahim;type=0